Kendi Kendine Çapraz Bağlama Silane - XLPE Bileşeni

Self-crosslinking Silane-XLPE Compound is a type of fast cross linking compound. It is recommended to be used for low-voltage wires and cables. It has following advantages: good electrical insulation properties, anti-aging properties and tensile strength; the highest continuous working temperature is 90ºC, excellent low-temperature brittleness properties.
Specification
YJZG-3 Self-crosslinking Silane-XLPE Compound for wires and cables.
Physical and Electrical properties
Processing Techniques
Melt extrusion temperatures in the range of 150ºC-200ºC are recommended, the specific temperature should be adjusted by actual operation condition.
Crossing-link rate
Cross-linking condition and time of the hot set elongation to 100% (1 mm thick samples): vapor or water bath at 90ºC for 15min or at 80ºC for 30min,Natural condition (23ºC/50%/48h).
Aging Test  
For excellent crossing-link, testing sample must be treated in vapor or hot bath (Minimum temperature:80ºC)
Storage and transport  
Self-crosslinking Silane-XLPE Compound for wires and cables should be vacuum packed, the aluminum foil / polyethylene combination film bag for inner packing and PP woven bag / PE / Kraft paper bag for outer. A group and B group are packed in different bags: A group net weight(23.75±0.02)kg while B group(1.25±0.02)kg. Negative tolerance of each-ton material is unexpected. Besides, other packaging agreed on by both manufacturers and clients can be used.
Keep away from sunshine, rain and soaking during transport. Store in clean, dry, ventilated warehouse and the minimum storage temperature  should be 0ºC.The product may be stored  for up to 6 months . And it must be used out once within 8 hours after the inner packaging is opened.