Temel bilgiler.
Yeniden kırılgan (°C)
1580 < yeniden kırılgan < 1770
Özellik
Uzun süreli malzemeler
Tip
Isıya dayanıklı Malzeme
Teknik Özelikler
230x114x65, 230x114x75
Ürün Açıklaması
Insulating Firebrick with light weight has high mini-porosity arranged in average, keep furnace wall low radiation. They can be used for hot face lining directly exposed to the heat or as a backup insulation layer. Light weight means the lowest thermal storage, it's quicker to heat and cool, and permit rapid cycle work. They are used for 800°C~1600°C.
Characteristic | Application |
Light weight and low thermal conductivity Maintain stable structural strength throughout ambient to maximum service temperature Low heat storage results in rapid cooling and heating operation Low iron and impurities to enhance reducing atmosphere; High thermal shock resistance in preventing spalling; Customize any size and shape High hot compressive strength | Lining of high-temperature kilns of industrial furnaces Annealing furnaces, Galvanizing furnaces Heat-treating furnaces, Air-heating furnaces Naphtha cracking furnaces, Ceramic shuttle kilns; Roller Kiln, Metal heat treatment furnaces; Steel billet reheating furnaces Oil refinery heaters, Laboratory furnaces, Reducing atmosphere furnace, Gas producers Furnaces backup insulation or heat face insulation |
Technical Data
Product Grade | Low Conductivity Type | High Strength Type | Bearing Type |
23 | 26 | 28 | 30 | 32 | B4 | B5 | B6 | B7 | C1 | C2 |
Classification Temperature | °C | 1260 | 1425 | 1538 | 1550 | 1600 | 1200 | 1300 | 1400 | 1500 | 1300 | 1400 |
Density | kg/m3 | 550-800 | 620-800 | 780-900 | 860-1000 | 870-1100 | 780 | 800 | 870 | 960 | 1100 | 1200 |
Reheat Shrinkage (°Cx8H) (JIS R2613) | % | 1300 0.2 | 1400 0.4 | 1500 0.4 | 1550 0.38 | 1600 0.38 | 1200 0.4 | 1300 0.5 | 1400 0.6 | 1500 0.9 | 1300 0.57 | 1400 0.59 |
Cold Crushing Strength (JIS R2615) | Mpa | 0.782.0 | 0.98 2.9 | 0.98 3.2 | 1.5 3.8 | 1.5 3.2 | 2.7 | 2.7 | 3.2 | 3.6 | 6.1 | 7.6 |
Modules of Rupture (JIS R2619) | Mpa | 0.69 1.2 | 0.78 1.4 | 0.98 1.7 | 1.5 1.7 | 1.3 1.7 | 1.6 | 1.7 | 2.0 | 2.0 | 2.5 | 3.1 |
Thermal Conductivity W/(m. K) 350°C (JIS R2616) | | 0.17 | 0.22 | 0.25 | 0.29 | 0.32 | 0.24 | 0.26 | 0.28 | 0.34 | 0.33 | 0.42 |
Thermal Expansion 1000°C (JIS R2617) | % | 0.46 | 0.44 | 0.48 | 0.47 | 0.48 | 0.5 | 0.5 | 0.48 | 0.5 | 0.50 | 0.51 |
Chemical Composition | Al2O3 | % | 41 | 63 | 66 | 67 | 72 | 40 | 40 | 41 | 68 | 40 | 41 |
SiO2 | % | 52 | 34 | 31 | 30 | 26 | 55 | 55 | 54 | 30 | 56 | 55 |
Fe2O3 | % | 0.9 | 0.9 | 0.7 | 0.6 | 0.6 | 1.3 | 1.3 | 1.4 | 0.9 | 1.3 | 1.2 |
Standard Size | mm | 230 X 114 X 65 ; 230 X 114 X 75 ; |
Adres:
17a, No. 445 Jiangning Road, Jing′an District, Shanghai, China
İşletme Türü:
Ticari Şirket
İşletme Aralığı:
Metalurji, Maden ve Enerji
Şirket Tanıtımı:
Şirketimiz, çok amaçlı taleplerinizi karşılayabilecek farklı ürün türleri konusunda uzmandır. Şirketin kuruluşlarını karşıladığından ve müşterilerimizin potansiyel ihtiyaçlarını karşılamak için her zaman elimizden gelen çabayı gösterdiğinden beri "önce kalite, önce müşteri ve kredi tabanlı" yönetim ilkelerine bağlıyız. Ekonomik küreselleşme trendi karşı konulmaz bir güçle geliştiğinden, kazançlı bir durum gerçekleştirmek için şirketimiz dünyanın dört bir yanından gelen kuruluşlarla işbirliği yapmaya samimi bir şekilde istekli.