Application: | Aviation, Electronics, Industrial, Medical, Chemical |
---|---|
Standard: | JIS, GB, DIN, ASTM |
Purity: | 90%Min |
Shape: | Sheet |
Alloy: | Alloy |
Secondary: | Non-secondary |
Doğrulanmış işletme lisanslarına sahip tedarikçiler
Alaşım | Derece | kimyasal bileşim yüzdesi | |||||
Mg | Al | Sn | MN (Min. | CE | ZR | ||
Mg | Mg99,95 | ≥ 99.95 | ≤ 0.01 | - | ≤ 0.004 | - | - |
Mg99,50 | ≥ 99.5 | - | - | - | - | - | |
Mg99,00 | ≥ 99.0 | - | - | - | - | - | |
MgAlZn | Az31B | Bal. | 2.5 - 3.5 | 0.60 - 1.4 | 0.20 - 1.0 | - | - |
AZ31S | Bal. | 2.4 - 3.6 | 0.50 - 1.5 | 0.15 - 0.40 | - | - | |
AZ31T | Bal. | 2.4 - 3.6 | 0.50 - 1.5 | 0.05 - 0.04 | - | - | |
AZ40M | Bal. | 3.0 - 4.0 | 0.20 - 0.80 | 0.15 - 0.50 | - | - | |
Az41M | Bal. | 3.7 - 4.7 | 0.80 - 1.4 | 0.30 - 0.60 | - | - | |
AZ61A | Bal. | 5.8 - 7.2 | 0.40 - 1.5 | 0.15 - 0.50 | - | - | |
AZ80A | Bal. | 7.8 - 9.2 | 0.20 - 0.80 | 0.12 - 0.50 | - | - | |
Az80M | Bal. | 7.8 - 9.2 | 0.20 - 0.80 | 0.15 - 0.50 | - | - | |
AZ80S | Bal. | 7.8 - 9.2 | 0.20 - 0.80 | 0.12 - 0.40 | - | ||
Az91D | Bal. | 8.5 - 9.5 | 0.45 - 0.90 | 0.17 - 0.40 | - | - | |
MgMn | M1C | Bal. | ≤ 0.01 | - | 0.50 - 1.3 | - | - |
M2M | Bal. | ≤ 0.20 | ≤ 0.30 | 1.3 - 2.5 | - | - | |
M2S | Bal. | - | - | 1.2 - 2.0 | - | - | |
MgZnZr | Zk61M | Bal. | ≤ 0.05 | 5.0 - 6.0 | ≤ 0.10 | - | 0.30 - 0.90 |
Zk61S | Bal. | - | 4.8 - 6.2 | - | - | 0.45 - 0.80 | |
MgMnRE | Me20M | Bal. | ≤ 0.020 | ≤ 0.30 | 1.3 - 2.2 | - | - |
Derece | Koşul | Çap/mm | Çekme Mukavemeti RM/MPa | Rp0.2/MPA | Uzama A/% |
AZ31B | H112 | ≤ 130 | 220 | 140 | 7.0 |
AZ40M | H112 | ≤ 100 | 245 | - | 6.0 |
100-130 | 245 | - | 5.0 | ||
Az41M | H112 | ≤ 130 | 250 | - | 5.0 |
AZ61A | H112 | ≤ 130 | 260 | 160 | 6.0 |
AZ61M | H112 | ≤ 130 | 265 | - | 8.0 |
Az80A |
H112 | ≤ 60 | 295 | 195 | 6.0 |
60-130 | 290 | 180 | 4.0 | ||
T5 | ≤ 60 | 325 | 205 | 4.0 | |
60-130 | 310 | 205 | 2.0 | ||
ME20M |
H112 |
≤ 50 | 215 | - | 4.0 |
50-100 | 205 | - | 3.0 | ||
100-130 | 195 | - | 2.0 | ||
ZK61M | T5 | ≤ 100 | 315 | 245 | 6.0 |
100-130 | 305 | 235 | 6.0 | ||
Zk61S | T5 | ≤ 130 | 310 | 230 | 5.0 |
Numbei | Derece | kimyasal bileşim yüzdesi | |||||
Al | Sn | MN (Min. | Si | Mg | |||
1 | YZMgAl2Si | YM102 | 1.9 - 2.5 | ≤ 0.20 | 0.20 - 0.60 | 0.7 - 1.20 | Bal. |
2 | YZMgAl2Si (B) | YM103 | 1.9 - 2.5 | ≤ 0.25 | 0.05 - 0.15 | 0.70 - 1.20 | Bal. |
3 | YZMgAl4Si (A) | YM104 | 3.7 - 4.8 | ≤ 0.10 | 0.22 - 0.48 | 0.60 - 1.40 | Bal. |
4 | YZMgAl4Si (B) | YM105 | 3.7 - 4.8 | ≤ 0.10 | 0.35 - 0.60 | 0.60 - 1.40 | Bal. |
5 | YZMgAl4Si (S) | YM106 | 3.5 - 5.0 | ≤ 0.20 | 0.18 - 0.70 | 0.5 - 1.5 | Bal. |
6 | YZMgAl2Mn | YM202 | 1.6 - 2.5 | ≤ 0.20 | 0.33 - 0.70 | ≤ 0.08 | Bal. |
7 | YZMgAl5Mn | YM203 | 4.5 - 5.3 | ≤ 0.20 | 0.28 - 0.50 | ≤ 0.08 | Bal. |
8 | YZMgAl6Mn (A) | YM204 | 5.6 - 6.4 | ≤ 0.20 | 0.15 - 0.50 | ≤ 0.20 | Bal. |
9 | YZMgAl6Mn | YM205 | 5.6 - 6.4 | ≤ 0.20 | 0.26 - 0.50 | ≤ 0.08 | Bal. |
10 | YZMgAl8Zn1 | YM302 | 7.0 - 8.1 | 0.40 - 1.00 | 0.13 - 0.35 | ≤ 0.30 | Bal. |
11 | YZMgAl9Zn1 (A) | YM303 | 8.5 - 9.5 | 0.45 - 0.90 | 0.15 - 0.40 | ≤ 0.20 | Bal. |
12 | YZMgAl9Zn1 (B) | YM304 | 8.5 - 9.5 | 0.45 - 0.90 | 0.15 - 0.40 | ≤ 0.20 | Bal. |
13 | YZMgAl9Zn1 (D) | YM305 | 8.5 - 9.5 | 0.45 - 0.90 | 0.17 - 0.40 | ≤ 0.08 | Bal. |
Derece | kimyasal bileşim/% | ||||||||||||||
Mg | Al | Sn | MN (Min. | YNT | ZR | AG | Y | Li | Bulunulabilecek | Si | FE | Cu | Ni | diğer | |
ZK51A | Bal. | - | 3.8 - 5.3 | - | - | 0.3 - 1.0 | - | - | - | - | ≤ 0.01 | - | ≤ 0.03 | ≤ 0.01 | ≤ 0.03 |
Zk61A | Bal. | - | 5.7 - 6.3 | - | - | 0.3 - 1.0 | - | - | - | - | ≤ 0.01 | - | ≤ 0.03 | ≤ 0.01 | ≤ 0.03 |
K1A | Bal. | - | - | - | - | 0.3 - 1.0 | - | - | - | - | ≤ 0.01 | - | ≤ 0.03 | ≤ 0.01 | ≤ 0.03 |
Zk41A | Bal. | - | 3.7 - 4.8 | ≤ 0.15 | 1.0 - 1.75 | 0.3 - 1.0 | - | - | - | - | ≤ 0.01 | ≤ 0.01 | ≤ 0.03 | ≤ 0.005 | ≤ 0.03 |
EZ33A | Bal. | - | 2.0 - 3.0 | ≤ 0.15 | 2.6 - 3.9 | 0.3 - 1.0 | - | - | - | - | ≤ 0.01 | ≤ 0.01 | ≤ 0.03 | ≤ 0.005 | ≤ 0.03 |
QE22A | Bal. | - | ≤ 0.20 | ≤ 0.15 | 1.9 - 2.4 | 0.3 - 1.0 | 2.0 - 3.0 | - | - | - | ≤ 0.01 | - | ≤ 0.03 | ≤ 0.01 | ≤ 0.03 |
QE22S | Bal. | - | ≤ 0.20 | ≤ 0.15 | 2.0 - 3.0 | 0.1 - 1.0 | 2.0 - 3.0 | - | - | - | ≤ 0.01 | ≤ 0.01 | ≤ 0.03 | ≤ 0.005 | - |
EQ21A | Bal. | - | - | - | 1.5 - 3.0 | 0.3 - 1.0 | 1.3 - 1.7 | - | - | - | ≤ 0.01 | - | 0.05 - 0.1 | ≤ 0.01 | ≤ 0.03 |
EQ21S | Bal. | - | ≤ 0.20 | ≤ 0.15 | 1.5 - 3.0 | 0.1 - 1.0 | 1.3 - 1.7 | - | - | - | ≤ 0.01 | ≤ 0.01 | 0.05 - 0.1 | ≤ 0.005 | - |
WE54A | Bal. | - | ≤ 0.20 | ≤ 0.15 | 1.5 - 4.0 | 0.3 - 1.0 | - | 4.75 - 5.5 | ≤ 0.2 | - | ≤ 0.01 | ≤ 0.01 | ≤ 0.03 | ≤ 0.005 | ≤ 0.03 |
WE43A | Bal. | - | ≤ 0.20 | ≤ 0.15 | 2.4 - 4.4 | 0.3 - 1.0 | - | 3.7 - 4.3 | ≤ 0.2 | - | ≤ 0.01 | ≤ 0.01 | ≤ 0.03 | ≤ 0.005 | ≤ 0.03 |
AZ31 | GB/T 5153 | |||||||
Güçlerince | Al | Sn | MN (Min. | Si | FE | Cu | Ni | Diğer, toplam |
Min. % | 2.40 | 0.50 | 0.15 | |||||
Maks. % | 3.60 | 1.50 | 0.4 | 0.10 | 0.005 | 0.05 | 0.005 | 0.3 |
AZ61 | GB/T 5153 | |||||||
Güçlerince | Al | Sn | MN (Min. | Si | FE | Cu | Ni | Diğer, toplam |
Min. % | 5.50 | 0.5 | 0.15 | |||||
Maks. % | 6.50 | 1.50 | 0.40 | 0.10 | 0.005 | 0.05 | 0.005 | 0.3 |
AZ91 | GB/T 5153 | ||||||||
Güçlerince | Al | Sn | MN (Min. | Si | FE | Cu | Ni | Bulunulabilecek | Diğer, toplam |
Min. % | 8.5 | 0.45 | 0.17 | 0.0005 | |||||
Maks. % | 9.5 | 0.90 | 0.40 | 0.08 | 0.004 | 0.025 | 0.001 | 0.003 | 0.3 |
AZ92 | AWS A5.19-1992 | ||||||||
Güçlerince | Al | Sn | MN (Min. | Si | FE | Cu | Ni | Bulunulabilecek | Diğer, toplam |
Min. % | 8.3 | 1.7 | 0.15 | 0.0002 | |||||
Maks. % | 9.7 | 2.3 | 0.50 | 0.05 | 0.005 | 0.05 | 0.005 | 0.0008 | 0.3 |