| Feature: | Oxidative Degradable |
|---|---|
| Material: | Polyamide(Nylon 6.66)/PA |
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Injection |
| Color: | White |
Doğrulanmış işletme lisanslarına sahip tedarikçiler
Denetlenen Tedarikçi https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html30% Glass Reinforced, Heat Stabilized, High Flow
| Product Description | |||
| Miramid® VE25C is a Polyamide 6 (Nylon 6) material filled with 25% glass fiber. It is available in Europe for injection molding. Important attributes of Miramid® VE25C are: Chemical Resistant Crystalline Fast Molding Cycle Good Stiffness Mold Release Agent Typical applications include: Engineering/Industrial Parts Automotive Construction Applications Electrical/Electronic Applications Sporting Goods | |||
| General | |||
| Form | Resin Pellets | ||
| Filler | 25 % Glass Fiber | ||
Feature |
Excellent Processability Crystalline Enhanced Stiffness Grease Resistant Solvent Resistant Good Stability |
Fuel Resistant High Mechanical Strength And Rigidity |
|
| Uses | Building Materials Automotive | Engineering Parts Electrical | Sporting Goods Mechanical Parts |
| Physical | Nominal Value | Test Method | |
| Dry: Density | 1.32 g/cm³ | ISO 1183 | |
| Dry: Water Absorption, Saturation | 7.3 % | ISO 62 | |
| Dry: Water Absorption, Equilibrium | 1.8 % | ISO 62 | |
| Dry: Viscosity Number | 145 cm³/g | ISO 307;ISO 1628;ISO 1157 | |
| Mechanical | Nominal Value | Test Method |
| Dry: Tensile Modulus | 8000 MPa | ISO 527-2 |
| Condition: Tensile Modulus | 5000 MPa | ISO 527-2 |
| Dry: Tensile Stress, Break | 160 MPa | ISO 527-2 |
| Condition: Tensile Stress, Break | 105 MPa | ISO 527-2 |
| Dry: Tensile Strain, Break | 3.0 % | ISO 527-2 |
| Condition: Tensile Strain, Break | 6.0 % | ISO 527-2 |
| Dry: Tensile Creep Modulus(1000 hr) | 3000 MPa | ISO 899-1 |
| Dry: Flexural Stress | 220 MPa | ISO 178 |
| Condition: Flexural Stress | 130 MPa | ISO 178 |
| Dry: Charpy Notched Impact Strength -30 °C 23 °C |
9.00 kJ/m² 10.0 kJ/m² |
ISO 179 1eA |
| Condition: Charpy Notched Impact Strength(23 °C) | 20.0 kJ/m² | ISO 179 1eA |
| Dry: Charpy Impact Strength -30 °C 23 °C |
50.0 kJ/m² 70.0 kJ/m² |
ISO 179 1eU |
| Condition: Charpy Impact Strength(23 °C) | 100 kJ/m² | ISO 179 1eU |
| Thermal | Nominal Value | Test Method |
| Dry: Deflection Temperature Under Load 0.45 MPa 1.8 MPa |
215 °C 205 °C |
ISO 75-2 |
| Dry: Melting Temperature, DSC | 220 °C | ISO 3146 |
| Electrical | Nominal Value | Test Method |
| Dry: Volume Resistivity | 1E+11 ohms·cm | IEC 60093 |
| Condition: Volume resistivity | 1E+8 ohms·cm | IEC 60093 |
| Dry: Dielectric Constant(1000000 Hz) | 3.50 | IEC 60250 |
| Condition: Dielectric Constant(1000000 Hz) | 6.00 | IEC 60250 |
| Dry: Dissipation Factor(1000000 Hz) | 0.020 | IEC 60250 |
| Condition: Dissipation factor(1000000 Hz) | 0.25 | IEC 60250 |
| Dry: Comparative Tracking Index | 550 | IEC 60112 |
| Processing | Nominal Value | |
| Processing Temp, Melt<Injection> | 260 - 290 °C | |
| Mold Temperature<Injection> | 80 - 120 °C |
Forever Co.,Ltd