Özellik: | Oksidatif bozunabilir |
---|---|
Malzeme: | Poliamit (Naylon 6.66)/PA |
Kullanım: | Genel plastikler, Mühendislik plastikleri, Özel plastikler |
Isıtılmış sonrasında plastik Özellikleri: | Termoplastik plastik plastik |
Plastik Form Verme Yöntemi: | Enjeksiyon |
Renk: | Beyaz |
Doğrulanmış işletme lisanslarına sahip tedarikçiler
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
TECHNYL STAR S 216 V30 NC is based on a patented high flow polyamide 6 resin (TechnylStar), reinforced with 30% of glass fibre, for injection moulding. Due to its outstanding flow caracteristics, this grade provides a significant productivity improvement and allows more freedom in mould and part design versus a standard polyamide solutions.
Product Description | ||||||
TECHNYL STAR S 216 V30 NC is based on a patented high flow polyamide 6 resin (TechnylStar), reinforced with 30% of glass fibre, for injection moulding. Due to its outstanding flow caracteristics, this grade provides a significant productivity improvement and allows more freedom in mould and part design versus a standard polyamide solutions. | ||||||
General | ||||||
Form | Resin Pellets | |||||
Filler | 30 % Glass Fiber | |||||
Rohs Ec 1907/2006 (Reach) Excellent Processability High Reflection |
||||||
|
||||||
Physical | Nominal Value | Test Method | ||||
Density | 1.34 g/cm³ | ISO 1183 | ||||
Water Absorption(24 hr;23 °C) | 0.95 % | ISO 62 | ||||
Molding shrinkage, parallel(50% RH;23 °C;72 hr) 0.2 % | ISO 2577;ISO 294- 4 |
|||||
Molding shrinkage, normal(50% RH;23 °C;72 hr) 0.75 % | ISO 2577;ISO 294- 4 |
Mechanical | Nominal Value | Test Method |
Dry: Tensile Modulus(1 mm/min) | 9600 MPa | ISO 527-1/-2 |
Condition: Tensile Modulus(1 mm/min) | 6200 MPa | ISO 527-1/-2 |
Dry: Stress at break | 180 MPa | ISO 527-1/-2 |
Condition: Stress at break | 110 MPa | ISO 527-1/-2 |
Strain at break | 3.3 % | ISO 527-1/-2 |
Dry: Flexural Modulus(2 mm/min) | 9300 MPa | ISO 178 |
Condition: Flexural Modulus(2 mm/min) | 5200 MPa | ISO 178 |
Flexural Strength(2 mm/min) | 255 MPa | ISO 178 |
Dry: Charpy Impact Strength(23 °C) | 81 kJ/m² | ISO 179/1eU |
Condition: Charpy Impact Strength(23 °C) | 90 kJ/m² | ISO 179/1eU |
Charpy Impact Strength, Unnotched(-30 °C) | 50 kJ/m² | ISO 179/1eU |
Dry: Charpy Notched Impact Strength(23 °C) | 10 kJ/m² | ISO 179 1eA |
Condition: Charpy Notched Impact Strength(23 °C) | 14 kJ/m² | ISO 179 1eA |
Dry: Izod Impact Strength, Unnotched(23 °C) | 82 kJ/m² | ISO 180/1U |
Condition: Izod Impact Strength, Unnotched(23 °C) | 65 kJ/m² | ISO 180/1U |
Dry: Izod Notched Impact Strength(23 °C) | 12 kJ/m² | ISO 180/1A |
Condition: Izod Notched Impact Strength(23 °C) | 19 kJ/m² | ISO 180/1A |
Thermal | Nominal Value | Test Method |
Melting Temperature(10°C/min) | 222 °C | ISO 11357-1 |
Temp. of deflection under load(1.8 MPa) | 204 °C | ISO 75 |
Flammability 1.5 mm 3 mm |
HB HB |
UL 94 |
Glow Wire Flammability Index(1.5 mm) | 650 °C | IEC 60695-2-12 |
Oxygen Index | 22 % | |
Electrical | Nominal Value | Test Method |
Volume Resistivity | 1E+11 ohms·cm | IEC 62631-3-1 |
Surface Resistivity | 1.0E+14 Ohms | IEC 62631-3-1 |
Comparative Tracking Index(Solution A) | 550 V | IEC 60112 |
Processing | Nominal Value |
Drying Temperature | 80 °C |
Dry Time(with a dehumidified air drying equipment, dew point mini -20°C) |
2 - 4 hr |
Suggested Max Moisture | 0.002 |
Rear Temperature | 230 - 235 °C |
Middle Temperature | 235 - 240 °C |
Front Temperature | 240 - 245 °C |
Mold Temperature | 60 - 90 °C |
.