| Feature: | Oxidative Degradable |
|---|---|
| Material: | Polyamide(Nylon 6.66)/PA |
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Injection |
| Color: | White |
Doğrulanmış işletme lisanslarına sahip tedarikçiler
Denetlenen Tedarikçi Nylon PA6 GF30 Glass Fiber Filled PA6 30% GF Virgin Grade PA6 10GF Materiahttps://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
30% Glass Reinforced, Medical grade
| Product Description | |||
| 30% Glass Reinforced, Medical grade | |||
| General | |||
| Form | Resin Pellets | ||
| Filler | 30 % Glass Fiber | ||
| Uses | Medical | ||
| Physical | Nominal Value | Test Method | |
| Dry: Density | 1.35 g/cm³ | ISO 1183 | |
| Dry: Melt Mass-Flow Rate, MFR(240 °C;2.16 kg) | 7.3 g/10min | ISO 1133 | |
| Dry: Melt Volume-Flow Rate, MVR(240 °C;2.16 kg) | 6.4 cm³/10 min | ISO 1133 | |
| Dry: Molding Shrinkage, Across Flow | 0.90 % | ISO 294-4 | |
| Dry: Molding Shrinkage, Flow | 0.30 % | ISO 294-4 | |
| Dry: Water Absorption, Saturation(23 °C) | 6.3 % | ISO 62 | |
| Dry: Water Absorption, Equilibrium(50% RH;23 °C) | 1.9 % | ISO 62 | |
| Dry: Shore Hardness, Shore D(15 sec) | 85 | ISO 868 | |
| Dry: Melt Density | 1.15 g/cm³ | ||
| Mechanical | Nominal Value | Test Method |
| Dry: Tensile Modulus | 9500 MPa | ISO 527-1 |
| Condition: Tensile Modulus | 6000 MPa | ISO 527-1 |
| Dry: Tensile Stress, Break | 180 MPa | ISO 527-2 |
| Condition: Tensile Stress, Break | 110 MPa | ISO 527-2 |
| Dry: Tensile Strain, Break | 3.5 % | ISO 527-2 |
| Condition: Tensile Strain, Break | 7.0 % | ISO 527-2 |
| Dry: Flexural Modulus | 8600 MPa | ISO 178 |
| Dry: Flexural Stress | 235 MPa | ISO 178 |
| Dry: Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 12 kJ/m² |
ISO 179/1eA |
| Condition: Charpy Notched Impact Strength -30 °C 23 °C |
11 kJ/m² 25 kJ/m² |
ISO 179/1eA |
| Dry: Charpy Unnotched Impact Strength -30 °C 23 °C |
75 kJ/m² 90 kJ/m² |
ISO 179/1eU |
| Condition: Charpy Unnotched Impact Strength -30 °C 23 °C |
75 kJ/m² 110 kJ/m² |
ISO 179/1eU |
| Thermal | Nominal Value | Test Method |
| Dry: Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
220 °C 200 °C |
ISO 75-2/B ISO 75-2/A |
| Dry: Melting Point(10 °C/min) | 220 °C | ISO 11357-3 |
| Dry: CLTE, Flow | 2.0E-5 cm/cm/°C | ISO 11359-2 |
| Dry: CLTE, Transverse | 7.0E-5 cm/cm/°C | ISO 11359-2 |
| Dry: RTI Elec 0.75 mm 3 mm |
65.0 °C 65.0 °C |
UL 746B |
| Dry: RTI Imp 0.75 mm 3 mm |
65.0 °C 65.0 °C |
UL 746B |
| Dry: RTI Str 0.75 mm 3 mm |
65.0 °C 65.0 °C |
UL 746B |
| Dry: Effective Thermal Diffusivity | 1.12E-7 m²/s | |
| Dry: Flame Rating 1.5 mm 3 mm 0.75 mm |
HB HB HB |
IEC 60695-11- 10;UL 94;IEC 60695-11-20 IEC 60695-11- 10;UL 94;IEC 60695-11-20 IEC 60695-11- 10;IEC 60695-11- 20 |
| Electrical | Nominal Value | Test Method |
| Condition: Surface resistivity | 1.0E+14 ohms | IEC 62631-3-2 |
| Dry: Volume Resistivity | 1E+11 ohms·cm | IEC 62631-3-1 |
| Condition: Volume resistivity | 1E+9 ohms·cm | IEC 62631-3-1 |
| Dry: Electric Strength | 30 kV/mm | IEC 60243-1 |
| Condition: Electric Strength | 25 kV/mm | IEC 60243-1 |
| Dry: Relative permittivity 1000000 Hz 100 Hz |
3.30 3.50 |
IEC 62631-2-1 |
| Condition: Relative Permittivity 1000000 Hz 100 Hz |
5.00 20.0 |
IEC 62631-2-1 |
| Dry: Dissipation Factor 100 Hz 1000000 Hz |
5.0E-3 0.015 |
IEC 62631-2-1 |
| Condition: Dissipation factor 100 Hz 1000000 Hz |
3000 1200 |
IEC 62631-2-1 |
| Condition: Comparative Tracking Index | 600 V | IEC 60112 |