Denetlenen Tedarikçi https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.htmlLNP KONDUIT PX10323 compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive.
| Product Description | |||
| LNP KONDUIT PX10323 compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added features of this grade include: Thermally Conductive. | |||
| General | |||
| Form | Resin Pellets | ||
| Filler | Glass Fiber | ||
| Feature Electrically Conductive Thermally Conductive | |||
| Consumer Industria Building and Construction |
Electrical | ||
| Physical | Nominal Value | Test Method | |
| Density | 1.61 g/cm³ | ASTM D792 | |
| Mold Shrinkage, Flow(24 hrs) | 0.2 % | ASTM D955 | |
| Mold Shrinkage, XFlow(24 hrs) | 0.22 % | ASTM D955 | |
| Moisture Absorption(50% RH;23 °C) | 0.04 % | ISO 62 | |
| Mechanical | Nominal Value | Test Method |
| Izod Impact, Unnotched 23 °C 80*10*4;23 °C |
73 J/m 6 kJ/m² |
ASTM D4812 ISO 180/1U |
| Izod Impact, Notched 23 °C 80*10*4;23 °C |
30 J/m 3 kJ/m² |
ASTM D256 ISO 180/1A |
| Tensile Stress, Break 5 mm/min;Type I 5 mm/min |
70 MPa 73 MPa |
ASTM D638 ISO 527 |
| Tensile Strain, Break 5 mm/min;Type I 5 mm/min |
0.9 % 0.8 % |
ASTM D638 ISO 527 |
| Tensile Modulus 5 mm/min 1 mm/min |
1.4E+04 MPa 1.4E+04 MPa |
ASTM D638 ISO 527 |
| Flexural Stress, Yield(1.3 mm/min;50 mm;span) | 96 MPa | ASTM D790 |
| Flexural Stress, break 1.3 mm/min;50 mm;span 2 mm/min |
95 MPa 96 MPa |
ASTM D790 ISO 178 |
| Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
1.4E+04 MPa 1.4E+04 MPa |
ASTM D790 ISO 178 |
| Impact Strength | 3.7 - 6.8 kJ/m² | ISO R179 |
| Thermal | Nominal Value | Test Method |
| Glow Wire Flammability Index 1 mm 1.6 mm |
850 °C 960 °C |
IEC 60695-2-12 |
| Glow Wire Ignition Temperature [GWIT](1 mm) | 825 °C | IEC 60695-2-13 |
| Heat Deflection Temperature[HDT], Unannealed(1.82 MPa;6.4 mm) | 204 °C | ASTM D648 |
| CTE, Flow(40°C to 120°C) | 1.2E-05 1/°C | ASTM E831 |
| CTE, XFlow(40°C to 120°C) | 7.3e-05 1/°C | ASTM E831 |
| Thermal conductivity through plane 60*60*3mm plaque 10*10*3mm sample |
1.5 W/m-K 3.5 W/m-K |
ISO 22007-2 ASTM E1461-07 |
| Thermal conductivity in plane 60*60*3mm plaque 25*0.4mm disc |
18 W/m-K 15 W/m-K |
ISO 22007-2 ASTM E1461-07 |
| HDT/Bf(0.45) | 217 °C | ISO 75/Bf |
| HDT/Af(1.8) | 201 °C | ISO 75/Af |
| Electrical | Nominal Value | Test Method |
| Surface Resistivity | 1.0E+06 ohms | ASTM D257 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 80 °C | |
| Drying Time<Injection> | 4 hrs | |
| Maximum Moisture Content<Injection> | 0.15 - 0.25 % | |
| Melt Temperature<Injection> | 270 - 295 °C | |
| Front, Zone 3 Temperature<Injection> | 270 - 290 °C | |
| Middle, Zone 2 Temperature<Injection> | 270 - 290 °C | |
| Rear, Zone 1 Temperature<Injection> | 260 - 275 °C | |
| Mold Temperature<Injection> | 85 - 100 °C | |
| Back Pressure<Injection> | 0.2 - 0.3 MPa | |
| Screw Speed<Injection> | 20 - 60 rpm |
Forever Co.,Ltd