Super Wear Resistant Hard facing Flux Cored Welding WireModle | Specification (φ, mm) | Hardness (HRC) | Composition |
ECI-60 | 2.8 | 58-62 | C:5%, Cr:28.6% |
ECI-80 | 2.8 | 60-64 | C:4.5%, Cr:25%, Nb:3.5% |
ECI-600 | 2.8,3.2 | 60-64 | C:4.5%, Cr:25%, W:3.5% |
ECI-WNi | 1.6,2.8,3.2 | 58-60 | C: 4.2%, Cr:25%, W:3.5%, Ni:1.2% |
ECI-100 Mo | 2.8 | 58-62 | C:4.5%, Cr:28, Mo:1% |
E-60 Wire & Welding Electrode Specification | Tubular wire : AS2576-2355 |
Welding rod : AS2576-2355 |
Material Type | High-chromium-high-carbon hard alloy on Fe-basis. |
Typical material analysis (wt %) |
C: 5.0 Cr: 28 Mn: 0.6 Si: 0.8 Fe: Balance |
Weld Deposit Characteristics | ECI-60 produces a wear-resistant, austenitic, primary carbide containing weld deposit. it is very resistant on abrasion. The material cannot be flame cut, offers good resistance to scaling and cannot be machined. The weld deposit exhibits cracks. |
Micro Structure | Chromium rich primary carbides in a carbide-austenite matrix. |
Weld Deposit Properties: | Hardness: 1st layer on Q235B SS400 56-60HRC |
2nd layer on Q235B SS400 58-62HRC |
Pure welding deposit : 60-63 HRC |
ASTM G65-04 Dry Sand Rubber Wheel Test Wear Expectation | The ASTM G65-04 dry sand rubber wheel test (Procedure A) wear |
expectation is less than 0.26 grams. |
Recommended Applications | Recommended particulary for the hard-facing of parts subjected to strong abrasion and average shock stress, e.g. screws,dredging bucket front edges, sieves, stirrer blades, sand slingers. top coats on dredger teeth and crushing rolls. Wear Plates. The application temperatures should not exceed 400ºC. |
|
|
Standard Sizes | Tubular wires: Φ1.6/2.0/2.4/2.8/3.2mm |
Packing:Mandrels 12.5kg |
Reels 25kg |
Drums 250kg |
Weld rods: Φ4.0/5.0/6.0mm |
Packing: 5kg packages |
Welding instructions for tubular wires | ECI-60 is welded without inert gas on the +pole(a.c. possible). Weave technique is usual. The arc should be held as short as possible and the thickness of hard-surfacing deposits should be limited to 10mm. Preheating decreases the generation of stress cracking on the hard-facing. |
Φ mm | 1.2 | 1.6 | 2 | 2.4 | 2.8 | 3.2 |
Current | 100-200 | 150-270 | 180-300 | 230-350 | 260-420 | 290-470 |
(A) |
Voltage | 16-22 | 24-27 | 25-28 | 26-29 | 27-30 | 28-30 |
(V) |
Stick out | 22-30 | 20-40 | 25-45 | 25-50 | 30-55 | 30-55 |
(mm) |
Welding instructions for welding rods: | ECI-60 welding rods can be welded with d.c. on the +pole but also with a.c. The height of the hard facing should be limited to 10mm.It is not necessary to re-dry the electrodes prior to welding. |
Φ mm | 3.25 | 4 | 5 | 6 |
Current(A) | 100-120 | 120-160 | 170-210 | 210-250 |
Ps.ECI-60 welding rods are high-performance electrodes with a deposition rate of 200%. |
Attentions | ☆The performance of weld overlay alloy is relevant to welding dilution rate. |
☆Prevent overheating while processing overly welding. |
☆If the base is too thin,it must be put under consideration that the base metal could become deformed. |
☆The control of electric current and voltage has a direct influence on the quality of overlay welding. |
☆if the cored wire is not used up after opening the drum,it must be preserve property with hermetic sealing to prevent from moisture and rusting. |
E-80 Wire & Welding Electrode Specification | Tubular wire: AS2576-2355 |
Welding rod: AS2576-2355 |
Material Type | High-niobium-high-carbon hard alloy on Fe-basis. |
Typical material analysis (wt %) |
C: 5.0 Cr: 27.5 Nb:3.5 Mn: 0.6 Si: 0.8 Fe: Balance |
Weld Deposit Characteristics | ECI-80 produces a wear-resistant, austenitic, primary carbide containing weld deposit. it is very resistant on abrasion. The material cannot be flame cut, offers good resistance to scaling and cannot be machined. The weld deposit exhibits cracks. |
Micro Structure | Niobium rich primary carbides in a carbide-austenite matrix. |
Weld Deposit Properties: | Hardness: 1st layer on Q235B SS400 56-60HRC |
2nd layer on Q235B SS400 58-62HRC |
Pure welding deposit : 60-64 HRC |
ASTM G65-04 Dry Sand Rubber Wheel Test Wear Expectation | The ASTM G65-04 dry sand rubber wheel test (Procedure A) wear expectation is less than 0.20 grams. |
Recommended Applications | Recommended particulary for the hard-facing of parts subjected to strong abrasion and medium impact, e.g. screws, dredging bucket front edges, sieves, stirrer blades. Top coats on dredger teeth and crushing rolls. Conveyor chute. Ventilator. Wear Plate. The application temperatures should not exceed 400ºC. |
|
|
Standard Sizes | Tubular wires: Φ1.6/2.0/2.4/2.8/3.2mm |
Packing:Mandrels 12.5kg |
Reels 25kg |
Drums 250kg |
Weld rods: Φ4.0/5.0/6.0mm |
Packing: 5kg packages |
Welding instructions for tubular wires | ECI-80 is welded without inert gas on the +pole(a.c. possible). Weave technique is usual. The arc should be held as short as possible and the thickness of hard-facing deposits should be limited to 10mm. Preheating decreases the generation of stress cracking on the hard-facing. |
Φ mm | 1.6 | 2 | 2.4 | 2.8 | 3.2 |
Current | 150-270 | 180-300 | 230-350 | 260-420 | 290-470 |
(A) |
Voltage | 24-27 | 25-28 | 26-29 | 27-30 | 28-30 |
(V) |
Stick out | 20-40 | 25-45 | 25-50 | 30-55 | 30-55 |
(mm) |
Welding instructions for welding rods: | ECI-80 welding rods can be welded with d.c. on the +pole but also with a.c. The height of the hard facing should be limited to 10mm.It is not necessary to re-dry the electrodes prior to welding. |
Φ mm | 3.25 | 4 | 5 | 6 |
Current(A) | 100-120 | 120-160 | 170-210 | 210-250 |
Ps. ECI-80 welding rods are high-performance electrodes with a deposition rate of 200%. |
Attentions | ☆The performance of weld overlay alloy is relevant to welding dilution rate. |
☆Prevent overheating while processing overly welding. |
☆If the base is too thin,it must be put under consideration that the base metal could become deformed. |
☆The control of electric current and voltage has a direct influence on the quality of overlay welding. |
☆if the cored wire is not used up after opening the drum,it must be preserve property with hermetic sealing to prevent from moisture and rusting. |
CTC6000 Wire Specification | Tubular wire: AS2576-2355 |
Material Type | High-wolfram-high-carbon hard alloy on Fe-basis. |
Typical material analysis (wt %) |
C: 5.0 Cr: 27.5 W:2-7 Mn: 0.6 Si: 0.8 Fe: Balance |
Weld Deposit Characteristics | CTC6000 produces a wear-resistant, austenitic, primary carbide containing weld deposit. it is very resistant on abrasion. The material cannot be flame cut, offers good resistance to scaling and cannot be machined. The weld deposit exhibits cracks. |
Micro Structure | Wolfram rich primary carbides in a carbide-austenite matrix. |
Weld Deposit Properties: | Hardness: 1st layer on Q235B SS400 56-60HRC |
2nd layer on Q235B SS400 58-62HRC |
Pure welding deposit : 60-64 HRC |
ASTM G65-04 Dry Sand Rubber Wheel Test Wear Expectation | The ASTM G65-04 dry sand rubber wheel test (Procedure A) wear expectation is less than 0.20 grams. |
Recommended Applications | Recommended particulary for the hard-facing of parts subjected to strong abrasion and medium impact, e.g. screws, dredging bucket front edges, sieves, stirrer blades. Top coats on dredger teeth and crushing rolls. Conveyor chute. Ventilator. Wear Plate. The application temperatures should not exceed 400ºC. |
|
|
Standard Sizes | Tubular wires: Φ1.6/2.0/2.4/2.8/3.2mm |
Packing:Mandrels 12.5kg |
Reels 25kg |
Drums 250kg |
Weld rods: Φ4.0/5.0/6.0mm |
Packing: 5kg packages |
Welding instructions for tubular wires | CTC6000 is welded without inert gas on the +pole(a.c. possible). Weave technique is usual. The arc should be held as short as possible and the thickness of hard-facing deposits should be limited to 10mm. Preheating decreases the generation of stress cracking on the hard-facing. |
Φ mm | 1.6 | 2 | 2.4 | 2.8 | 3.2 |
Current | 150-270 | 180-300 | 230-350 | - 420
| 290-470 |
(A) |
Voltage | 24-27 | 25-28 | 26-29 | 27-30 | 28-30 |
(V) |
Stick out | 20-40 | 25-45 | 25-50 | 30-55 | 30-55 |
(mm) |
Attentions | ☆The performance of weld overlay alloy is relevant to welding dilution rate. |
☆Prevent overheating while processing overly welding. |
☆If the base is too thin,it must be put under consideration that the base metal could become deformed. |
☆The control of electric current and voltage has a direct influence on the quality of overlay welding. |
☆if the cored wire is not used up after opening the drum,it must be preserve property with hermetic sealing to prevent from moisture and rusting. |
Company IntroductionGST International Engineering (GaoShengTai), is a Sino-Australian joint venture company with an ISO 9001 Certified wear plate production & fabrication workshop, facility located in Qingdao City, China. Our partner -- Enduraclad International (ECI) is an Australian based privately owned company with an ISO 9001 Certified workshop facility located in Western Australia, along with a large fabrication workshop in Queensland. GST is an independent 'one stop shop' provider of wear solutions with an emphasis on Wear resistant products. To support their workshop facilities GST employ a direct supply chain with National and International coverage.GST's approach to continuous research and development allows them to be considered a front runner in wear plate & hard-facing welding wire technology. Their products have a proven track record of success in many fields. Their "anything is possible" attitude makes them the go to business for improving wear and impact protection where other suppliers fail.FAQQ: Are you trading company or manufacturer?A: We are manufacturerQ: Are you able to produce customized chemical composition and dimension?A: Yes, we can customized all your needs. Q: How long is your delivery time?A: Depending on the quality required. Q: Do you provide samples ? is it free or extra?A: We can provide free sample, the buyer will bare the freight cost. Freight charges will deduct from the first order.Q: What are your terms of payment?A: T.T before delivery. Q: Do you provide after-sales service?A: Yes
Adres:
Xiao Wang, Ge Zhuang Cun, Jiaobei Street Office, Jiaozhou City, Qingdao City, Shangdong Province, China
İşletme Türü:
Üretici/Fabrika, Ticari Şirket
İşletme Aralığı:
Araçlar ve Donanım, Endüstriyel Ekipmanlar ve Bileşenleri, Metalurji, Maden ve Enerji
Yönetim Sistemi Sertifikasyonu:
ISO 9001
Şirket Tanıtımı:
GST Çevre Koruma Teknolojisi Co., Ltd. (Şirket Grubu: Suzhou GST aşınmaya dayanıklı Birleşik Malzeme Co., Ltd.; Enduraclad Uluslararası Mühendislik-Qingdao; Enduraclad International-Australia) Shandong Provence′nin doğu kısmında yer alır -- Çin’in en modern ve güzel deniz manzaralı şehridir ve başkenti Pekin’e yaklaşık 600 km uzaklıktadır. GS Tec, teknolojik AR-GE, üretim, satış ve pazarlama ve dış kaynak kullanımı hizmetleri konularında uzman ileri teknoloji şirketlerinden biri. Fikri mülkiyet hakları olan ana ürünlerimiz TBSP-1 ve TBSP-2 Nano seramik antikorozyon kaplı malzeme ve KFM-1, KFM-2, KGFM-1 ve KGFM-2 serisi kompozit seramik malzeme ile TBST-WD-01 TBST-WF-01 Serisi Çelik Yapı kaplamadır.
Ürünler çevre dostudur ve kömür-yangın enerji santrali, kimyasal, petrol ve ilaç endüstrilerinde yaygın olarak kullanılmaktadır.
Bu arada 2019 yılında, dağıtılmış optik fiber algılama teknolojisini tanıttık ve dağıtılmış sıcaklık algılama ve dağıtım gibi bir dizi optik fiber ürünü geliştirdik. Enerji, petrol, petrokimya, petrol ve gaz gibi enerji ile ilgili endüstriler için uygundur.
Şu anda GST′nin ürünleri IS09001, IS014001 sistem sertifikasını almıştır ve ana ürünler ilgili yurt içi ve yurt dışı profesyonel test Enstitüsü performans test teknolojisi tarafından onaylanmıştır.
GST, karşılıklı olarak faydalı bir ortaklık oluşturmak için sizinle işbirliği yapmak istiyor.