Metal Filtration Silicon Carbide Ceramic Foam Filter

• Yeniden kırılgan (°C): 1500
• Özellik: Foam Filter
• Tip: Ceramic Foam Filter
• Şekil: Plaka
• Malzeme: Silicon Carbide
• inç başına gözeneklilik (ppi): 10-60
• Hayır. Modeli.: ceramic foam filter
• hacim ağırlığı: 0.35 - 0,5g/cm3
• sıkıştırma mukavemeti: 0,9 mpa
• Taşıma Paketi: Cartons Palletized
• Teknik Özelikler: as custom
• Ticari Marka: XingFeng
• Menşei: China
• HS Kodu: 84219990
• Üretim Kapasitesi: 50000m3 Per Year

Ürün Açıklaması

Metal Filtration Silicon Carbide Ceramic Foam Filter

Silicon Carbide Ceramic Foam Filters mainly for filtration of cast iron and non-ferrous alloys. With their excellent resistance to attack and corrosion from molten iron liquid, they can effectively remove inclusions, reduce trapped gas from liquid metal and provide laminar flow, and then the filtered metal is significantly cleaner. Cleaner metal results in higher-quality castings, less scrap, and fewer inclusion defects, all of which contribute to bottom-line profit.

SiC Ceramic Foam Filters (CFF-SC) is available in all standard dimensions and different thickness. The most common porosities are PPI 10, 20 and 30; higher porosities are available upon request. Custom-made cut-to-size filters are also possible.

SiC Ceramic Foam Filters (CFF-SC) common sizes in Round shape:

40x11mm, 40x15mm, 50x15mm, 50x20mm, 60x22mm,
70x22mm, 80x22mm , 90x22mm,100x22mm, 305x25mm

SiC Ceramic Foam Filters (CFF-SC) common sizes in Square shape:

40x40x11mm, 40x40x15mm, 50x50x22mm, 75x75x22mm, 50x75x22mm, 
100x75x22mm, 100x100x22mm, 55x55x15mm, 150x150x22mm

Physical Properties for SiC Ceramic Foam Filters (CFF-SC):

Working Temperature	≤1540°C
Porosity	80~90%
Compression Strength  (Room Temperature)	≥1.0Mpa
Volume Density	0.3-0.5g/cm^3
Thermal Shock Resistance	1200°C---room temperature 3 times
Application	cast iron, cast copper,  cast bronze, cast brass high temperature gas filter, chemical fillings and catalysis carrier

Chemical Composition for SiC Ceramic Foam Filters(CFF-SC):

Al2O3	SiC	SiO2	Fe2O3
≤28.00%	≥62.00%	≤10.00%	≤0.50%